p.  1

SPEC DATA®

Sheet Metal Roofing 07610 Petersen Aluminum Corporation

1 PRODUCT NAME a combination of 70% Kynar 500® Aluminum Structures
PAC-CLAD® - Prefinished Sheet polyvinylidenefluoride (PVDF), acrylic American Iron and Steel Institute
Aluminum & Steel resins, pigments and solvents. The (AISI)
system consists of Fluropon® top • AISI G90 -Hot Dipped Galvanized
2 MANUFACTURER coat applied over a polyester primer. Steel Sheet, Commercial Weight
Petersen Aluminum Corporation A wash coat is applied to the reverse • Specifications for Cold-Formed
1005 Tonne Road side for additional protection. Steel Design Manual
Elk Grove Village, IL 60007
P: 800-323-1960 Standard Sizes: Aluminum is American Society for Testing &
847-228-7150 available in .032” -.080” (0.8 – 2 mm) Materials (ASTM)
F: 800-722-7150 thickness in 48” (1219 mm) widths. • ASTM A525 – Steel Sheet,
www.pac-clad.com Galvanized steel is available in 24 ga Zinc-Coated by the Hot Dip Process
in 48” (1219 mm) widths. • ASTM A653/A653-97 – Steel Sheet,
3 PRODUCT DESCRIPTION Zinc-Coated (Galvanized) by the
PAC-CLAD is a pre-finished Special Sizes: Aluminum is available Hot Dip Process, Structural
specification grade aluminum sheet in thickness to .125” (3.2 mm) and in Physical Quality
or a commercial quality extra-smooth widths to 60” (1524 mm) on special • ASTM B117-95 – Operating Salt
galvanized steel sheet, primed order. Minimum quantity is 20,000 Spray (Fog) Apparatus
and coated with Petersen’s full lb (9080 kg). Galvanized steel is • ASTM B209/B209M-97 – Aluminum
strength fluoropolymer (PVDF) high- available in gauges from 26 – 18 and and Aluminum Alloy Sheet and Plate
performance coating system of 1.0 in widths up to 60” (1525 mm) on • ASTM D523-89(1994)el –
mil (0.025 mm) total dry film thickness special order. Minimum quantity is Spectral Gloss
and, on the reverse side, a wash coat 20,000 lb (9080 kg). • ASTM D659 – Discontinued
of 0.3 – 0.4 mil (0.008 – 0.01 mm) dry standard replaced by ASTM D4214
film thickness. Colors: For standard colors, refer to • ASTM D968-93 – Abrasion
Table 1. Custom match colors are Resistance of Organic Coatings by
Basic Use: PAC-CLAD is for available in minimum quantities of Falling Abrasive
general sheet metal use in building 10,000 lb (4540 kg). • ASTM D1737-97 – Discontinued
applications. PAC-CLAD is frequently standard, replaced by ASTM D522
used in the following forms: Finish: Sheens available – Dull, • ASTM D1808 -Discontinued
• Fascia and soffit panels matte and specular, gloss rating of 25 standard
• Gravel stops and copings – 35% at 60° viewing angle. Textures • ASTM 2247-94 – Testing Water
• Store front components available: Smooth; stucco Resistance of Coatings in 100%
• Roofing and mansard panels: embossed texture E-5. Relative Humidity
flat, batten and standing • ASTM 2794-93 – Resistance of
seam types Limitations: PAC-CLAD performance Organic Coatings to the Effects of
depends on the integrity of the Rapid Deformation (Impact)
Materials and Finishes: PAC- coating film, and in galvanized steel, • ASTM 3281 – Discontinued
CLAD consists of either Aluminum on the underlying coating of zinc. standard
Association specification ASTM B209 PAC-CLAD should not be used in • ASTM 3359-95a – Measuring
aluminum sheet, temper H14 or H34, areas of high abrasion or where it will Adhesion by Tape Test
or hot-dipped ASTM A 653 Grade be subject to mechanical damage. • ASTM D3363-82e1 – Film Hardness
A structural quality steel sheets, AISI G90 galvanized, commercial TECHNICAL DATA 4 by Pencil Test • ASTM G23-96 – Operating Light
weight. PAC-CLAD sheets are Applicable Standards: Aluminum Exposure Apparatus (Carbon Arc
coated with a 2-coat system using Association – Specifications for Type) With and Without Water

SPEC-DATA®

SPEC-DATA® and MANU-SPEC® are registered trademarks of Reed Elsevier Inc. The three part MANU-SPEC format conforms to the editorial style of The Construction Specifications Institute and is used with their permission. The manufacturer is responsible for technical accuracy. ©2007 Reed Construction Data. All Rights Reserved.

SPEC-DATA®

Factory Mutual (FM) – Loss Prevention Data Sheets 1-7 and 1-49

National Coil Coaters Association (NCAA)

  • NCAA Procedure No. 11-5
  • NCCA Procedure No. 11-18
  • NCCA Technical Bulletin No. 11-6

Sheet Metal & Air Conditioning Contractors National Association, Inc. (SMACNA) -Architectural Sheet Metal Manual

Physical Properties of Fluoropolymer Coating:

  • Abrasion Resistance – ASTM D968, coefficient of sand abrasion 65 ± 10
  • Accelerated Weathering, Chalk ASTM G23, Type EH, 5000 hours, rating of 8 or better
  • Accelerated Weathering, Color ASTM G23. Type EH, 5000 hours,

≤ 5 ∆E (Hunter Units) color change

  • Adhesion – ASTM D3359/NCCA Procedure No. 11-5 cross-cut tape test, pass
  • Chalk Resistance – ASTM D659, no chalk rating 9 – 10
  • Color Change – 20 years, ≤ 5 ∆E

(Hunter Units) change, after removal

of external deposits

    • Chemical/Acid Pollution Resistance
    • – ASTM D1808; pass, no color change
  • Formability – ASTM D3281 and ASTM D1737, can be formed without film fracture using normal shop practices to a 1 to 2-T bend radius
  • Gloss – ASTM D523 Specular gloss of 30° + 5 (low gloss/sheen available) at 60; 26 ga PAC-CLAD GLOSS 10 +5 AT 60°
  • Hardness – ASTM D3363 -≥ F

pencil hardness

  • Humidity Resistance – ASTM D2247, 1000 hours, no change in hardness
    • •
    Impact Resistance – ASTM D2794 and NCCA Technical Bulletin No. 11-6, 70 lb-inch (7.9 Nom.), no tape pick-off
• Life Expectancy – ASTM G23. Type
EM, weatherometer, 5000 hours,
chalk rating of 8 or better
• Salt Spray Resistance, Aluminum –
ASTM B117, 2000 hours, creepage
at scribe ≤ 1/32” (0.8 mm), no
blisters
• Salt Spray Resistance, Steel – ASTM
B117, 1000 hours, creepage at
scribe ≤ 1/8” (3.2 mm), few #8
blisters
• Solvent Resistance – NCCA 7
procedure 11-18, (no comparable
ASTM test), pass
INSTALLATION5
Methods: Fabricate and install PAC
CLAD sheet metal in accordance
with SMACNA sheet metal practices. 8

PAC-CLAD can be cut, formed, nailed, screwed or riveted using conventional hand or power tools. PAC-CLAD coatings must be mechanically removed if soldering or welding are necessary. For best results, cutting edges should be kept sharp, clean, properly dressed and closely aligned. 9

A strippable vinyl film can be applied for protection during fabrication and installation is desired. Vinyl film may remain on the coating during 10 fabrication and erection. Vinyl must be removed prior to or immediately after installation.

PAC-CLAD is a finished material; care must be taken during fabrication and erection to avoid damage to the surface. Proper bend radii must be used in fabrication.

6 AVAILABILITY & COST Availability: PAC-CLAD panels are available nation-wide and are stocked in standard colors for rapid shipping within 72 hours. Special finishes require additional time for color matching and approvals.

There is a 20,000 lb (9080 kg) minimum for non-standard widths and colors. Delivery time and price will be quoted upon inquiry.

Cost: Cost for PLAC-CLAD panels is generally 60% of copper roofing sheet, 25% to 50% less than hardcoat anodized finishes and approximately equal to shop or field painted galvanized steel. Contact the manufacturer for specific costs.

WARRANTY

A 20-yeaar, non-prorated warranty covering color, fade, chalking and film integrity is available at no additional cost. The warranty is issued on a per project basis upon request.

MAINTENANCE

Maintenance is not required. The panel finish is a member of the Teflon® family and is self-cleaning. If cleaning is desired, panels can be washed with mild soap and water followed by a clean water rinse.

TECHNICAL SERVICES

Technical services are available from Petersen Aluminum Corporation and regional architectural representatives.

FILING SYSTEMS
  • Architects’ First Source for Products
  • MANU-SPEC®
  • Sweet’s Catalog Files

SPEC-DATA® and MANU-SPEC® are registered trademarks of Reed Elsevier Inc. The three part MANU-SPEC format conforms to the editorial style of The Construction Specifications Institute and is used with their permission. The manufacturer is responsible for technical accuracy. ©2007 Reed Construction Data. All Rights Reserved.

PAC-CLAD Color Availability

PAC-CLAD Standard Reflectivity Emissivity 3 Year Exposure SRI* Steel 24ga. 22ga. .032 Aluminum .040 .050 .063
Almond 0.56 0.89 0.57 66 √ √ √ √ √
Bone White 0.73 0.89 0.71 89 √ √ √ √ √ √
Cardinal Red 0.37 0.89 0.38 41 √ √ √
Charcoal 0.28 0.89 29 √ √ √
Colonial Red 0.32 0.89 34 √ √ √ √
Dark Bronze 0.25 0.89 25 √ √ √ √ √ √
Evergreen 0.26 0.88 26 √ √
Granite 0.36 0.89 0.35 40 √ √ √ √ √
Hemlock Green 0.30 0.90 32 √ √ √ √
Hunter Green 0.26 0.88 26 √ √
Mansard Brown 0.25 0.88 25 √ √ √ √ √
Medium Bronze 0.27 0.90 28 √ √ √ √ √ √
Military Blue 0.34 0.88 36 √ √
Musket Gray 0.31 0.89 33 √ √ √ √
Patina Green 0.34 0.89 37 √ √
Sandstone 0.53 0.89 0.49 62 √ √ √ √ √ √
Sierra Tan 0.36 0.89 0.35 40 √ √ √ √ √
Slate Blue 0.26 0.87 26 √ √
Slate Gray 0.36 0.89 40 √ √ √ √ √
Stone White 0.64 0.88 0.59 77 √ √ √ √ √ √
Teal 0.26 0.88 26 √ √
Terra Cotta 0.36 0.89 0.37 40 √ √ √
Matte Black** 0.25 0.85 23 √ √ √ √ √

PAC-CLAD Metallic

Aged Copper 0.28 0.89 29 √ √ √
Champagne 0.41 0.80 0.40 43 √ √ √
Copper Penny 0.49 0.87 0.47 56 √ √ √ √
Silver 0.60 0.83 0.55 70 √ √ √ √
Weathered Zinc 0.30 0.81 28 √ √ √
Zinc 0.32 0.89 0.31 34 √ √ √

SPEC-DATA®

PAC-CLAD Standard Colors (do not meet cool roof requirements)

Arcadia Green √ √
Award Blue √ √ √
Berkshire Blue √
Burgundy √ √ √
Forest Green √ √ √ √ √
Hartford Green √ √ √ √
Interstate Blue √ √ √

SPEC-DATA® and MANU-SPEC® are registered trademarks of Reed Elsevier Inc. The three part MANU-SPEC format conforms to the editorial style of The Construction Specifications Institute and is used with their permission. The manufacturer is responsible for technical accuracy. ©2007 Reed Construction Data. All Rights Reserved.

Download Adobe Flash Player.