Technical Data for Kynar 500/Hylar 5000 Coating:

• South Florida Exposure:  Color (ASTM D 2244) – No more than 5ΔE Hunter units at 20 years; Chalk (ASTM D 4214) – Rating no less than 8 at 20 years; Film integrity – 20 years.

• Accelerated Weathering (ASTM D 4587, ASTM G 154):  5000 Hours; Chalk, per ASTM D 4214, rating of 6 or better; Color, per ASTM D 2244, < 5ΔE (Hunter Units) color change.

• Humidity Resistance (ASTM D 2247): Galvalume or HDG, 100% RH, 2000 hours – No field blisters; Aluminum, 100% RH, 3000 hours – No field blisters

• Salt Spray Resistance (ASTM B 117): Aluminum, 3000 hours, Galvalume or HDG, 1000 hours – Creep from scribe no more than 1/16”, no field blisters

• Chemical/Acid Pollution Resistance (ASTM D 1308): Pass

• T-Bend (ASTM D 4145): 1T – 3T with no loss of adhesion

• Pencil hardness (ASTM D 3363): HB – 2H

• Specular Gloss (ASTM D 523) @ 60 degrees: Typical – 20 – 35

• Abrasion Resistance (ASTM D 968): 67 +/- 10 liters

• Cross Hatch Adhesion (ASTM D 3359): No loss of adhesion

• Reverse Impact (ASTM D 2794): Galvalume or HDG, 2x metal thickness inch-pounds, no loss of adhesion; Aluminum, 1.5x metal thickness inch-pounds, no loss of adhesion

• Flame Test (ASTM E 84) – Class A coating